Capacity
2,20,000
TPA
Equipment
- Reheating Furnace fully automated with dual fired burner LPG/LDO.s
- High-pressure De-scaler.
- 4-Stand Housingless Roughing Mill in horizontal and vertical combination.
- 10-Stand Housingless Continuous Mill in horizontal/vertical combination with 8 loopers for tension free rolling and 2 shears for end cutting.
- 4–Cantilever stands in horizontal and vertical combination with Tungsten Carbide (TC) Rings.
- 10-Stand V-type, no twist wire rod block.
- Primary cooling line for controlling laying temperature.
- Laying head.
- 70 m long cooling conveyor with retarded, forced cooling and online quenching facility.
- Pallet type coil handling with vertical compactor.
- Mill fully automated by ABB drive and PLC.
- Solution Annealing Furnace.
- Pickling line with Effluent Treatment Plant.
- Wendt CNC grinding machine for TC Rings.
Product Specifications
| SIZE RANGE | COIL WEIGHT | COIL DIMENSIONS | TOLERANCE | SUPPLY CONDITION | |
|---|---|---|---|---|---|
| WIRE ROD | 5.5 – 16 mm (Wire rod block ) |
850 kg | ID: 800 – 900 mm OD: 1250 (wire rod block) | As per EN 10088 | Hot rolled (HR) Hot rolled + pickled (HRP) |
| (Available in mm) 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10, 11, 12, 13, 14, 15 and 16. | 50 kg 25 kg |
Hot rolled + annealed + pickled (HRAP) | |||
| Under commissioning: 17 – 40 mm (garret coiled) |
GRADES
ASTM: 201, 202, 204Cu, 301, 302, 303, 304, 304Cu, 304HC, 304L, 304H, 310, 310S, 312, 314, 316, d16L, 316LN, 316Ti, 316LCu, 321, 410, 420, 430, 430L, 904L
DIN/EN: 1.4301, 1.4306, 1.4307, 1.4310, 1.4401, 1.4404, 1.4567, 1.4841, 1.4842, 1.4541, 1.4845, 1.4570, 1.4571, 1.4578, 1.4597, 1.4362, 1.4370 and 1.4016
Electrode Grades: ER304, ER304L, ER307, ER307SI, ER308, ER308L, ER308LSi, ER310, ER316, ER316L, ER316LSi, ER347, ER347SI, ER309L, ER430 and ER420
*Specialised grades also available as per customer requirements.
MECHANICAL TESTING DATA
HOT ROLLED WIRE ROD
| HOT ROLLED WIRE ROD | ||||
|---|---|---|---|---|
| GRADE | UTS (Kg/mm2) | YS (Kg/mm2) | EL% | RA% |
| SS 201 (SUPER) | 880 Max. | 500 Max. | 50 Min. | 65 Min. |
| SS 201 (NI-1%) | 880 Max. | 480 Max. | 50 Min. | 65 Min. |
| SS 204Cu | 780 Max. | 450 Max. | 50 Min. | 65 Min. |
| SS 202 (NI-4%) | 780 Max. | 450 Max. | 50 Min. | 65 Min. |
| AISI 304 | 700 Max. | 380 Max. | 50 Min. | 70 Min. |
| AISI 304 L | 700 Max. | 380 Max. | 50 Min. | 70 Min. |
| AISI 304 H | 700 Max. | 380 Max. | 50 Min. | 70 Min. |
| AISI 304 Cu2 | 680 Max. | 350 Max. | 50 Min. | 70 Min. |
| ER 307 | 700 Max. | 380 Max. | AISI 310 | 70 Min. |
| ER 308L | 700 Max. | 380 Max. | 50 Min. | 70 Min. |
| 308 LSi | 700 Max. | 380 Max. | 50 Min. | 70 Min. |
| AISI 310 | 680 Max. | 450 Max. | 50 Min. | 70 Min. |
| AISI 316 L | 660 Max. | 400 Max. | 50 Min. | 70 Min. |
| ER 316 L | 660 Max. | 400 Max. | 50 Min. | 70 Min. |
| AISI 316 LHMo | 680 Max. | 400 Max. | 50 Min. | 70 Min. |
| SS 430L | 580 Max. | 450 Max. | 30 Min. | 65 Min. |
HOT ROLLED ANNEALED WIRE ROD
| GRADE | UTS (Kg/mm2) | YS (Kg/mm2) | EL% | RA% | HARDNESS |
| SS 204Cu | 680 Max. | 360 Max. | 50 Min. | 65 Min. | |
| AISI 304 | 600 Max. | 300 – 350 | 60 Min. | 70 Min. | 22 Max. |
| AISI 304 L | 580 Max. | 300 – 350 | 60 Min. | 70 Min. | 22 Max. |
| AISI 304 u2 | 580 Max. | 300 – 350 | 60 Min. | 70 Min. | 22 Max. |
| ER 308L | 580 Max. | 300 – 350 | 60 Min. | 70 Min. | 22 Max. |
| AISI 316 L | 550 Max. | 250 Max | 60 Min. | 70 Min. | 22 Max. |
| ER 316 L | 550 Max. | 250 Max | 60 Min. | 70 Min. | 22 Max. |
| AISI 316 LHMo | 580 Max. | 320 Max | 50 Min. | 70 Min. | 22 Max. |
| SS 430L | 480 Max. | 300 Max | 40 Min. | 70 Min. | 85 Max. HRB |